CLASSIFICATION

EN 14700 T Fe10

DESCRIPTION

• Tubular wire for gas shielded metal arc hardfacing
• Austenitic stainless weld deposit
• Good impact, cavitation and corrosion resistance
• The weld deposit work hardens to different degrees depending on amount of impact
• Resists scaling up to 850°C, good resistance to thermal shocks

APPLICATIONS

• Hardface 19 9 6-G is mainly used to rebuild components exposed to high impact and corrosion.
• Sub-layer before hardfacing 

Examples
Steel mill rolls, metallurgical plant guides, tram and train rails and fittings, high speed forming rolls

TYPICAL ALL-WELD METAL ANALYSIS CMnSiCrNi

0.10

6.00

0.50

19.0

9.0

Structure: austenite

TYPICAL ALL-WELD METAL MECHANICAL PROPERTIES Hardness – 3-Layer deposit: As welded 180 HBWork hardened: 47 HRc CONDITIONS OF USE Current typeShielding gas

DC (+)

EN ISO 14175

M12 / M13 / M20 / M21

OPERATING CONDITIONS Diameter
[mm]Amperage [A]Voltage [V]Stick-out [mm]Gas flow [l/min]

1.2	100 - 300	24 - 32	12 - 25	10 - 20
1.6	150 - 300	24 - 32	12 - 25	10 - 20
2.0	200 - 400	24 - 32	12 - 30	10 - 20
2.4	250 - 450	24 - 32	12 - 30	10 - 20

Recovery: > 95 %

WELDING POSITIONS

Hardface 19 9 6-G, up to Ø 1.6 mm, is suitable as well for downhand as for positional welding by adapting transfer mode and welding parameters as for solid

STANDARD DIAMETERS (mm)

1.2, 1.6, 2.0, 2.4
Other diameters: please consult us

PACKAGING Diameter≤  2.4 mm≥   2.4 mm

Standard packaging [EN ISO 544]	Spool : BS 300	Coil : B 450	Drum
Weight	15 kg	25 kg	Up to 330 kg

Other packaging: please consult us