英国进口MWA工模具焊条MAC TOOL E3064|H13工具钢

A low hydrogen, iron powder basic flux coated electrode. Designed for special hardfacing applications involving heavy impact loading combined with abrasion. This electrode is ideally suited for forging dies because of its very tough deposit. It is an H13 type product. Pre-heat and dilution may effect hardness on first two layers but not on subsequent layers. On heavy build-ups use Mac Trode E6718 as buffer layer on carbon steels and Mac Trode E630 on 13% manganese steels

Mac Tool E3064为低氢铁粉碱性焊剂涂层焊条，专为涉及剧烈冲击载荷和磨损的特殊硬面堆焊应用而设计。该款焊条熔覆层非常坚硬、耐高温性能佳，特别适合锤锻模。它是H13型产品。预热和稀释可能会影响前两层的硬度，但不会影响后续熔敷层的硬度。对于厚堆焊，在碳钢上使用Mac Trode E6718 作为缓冲层，在13%锰钢上使用Mac Trode E630。

1. Resists Heavy Impact. 抗剧烈冲击。
2. Ideal for Hammer Dies. 非常适合锤锻模。
3. Good High Temperature Resistance. 良好的耐高温性。
4. Weld Deposit Matches H13 Steel. 熔敷层与H13钢匹配。
5. Weld Metal Hardness 50-56HRC. 焊缝金属硬度50-56HRC。

Typical All Weld Metal Chemical Analysis (%)

典型全焊缝金属成分

Typical All Weld Deposit Hardness

典型全焊缝金属熔敷层硬度：

1st Layer第一层：53-55HRC(560-600HV)

2nd Layer第二层：56-60HRC(620-680HV)

3rd Layer第三层：57-60HRC(640-680HV)

Sizes Available and Recommended Amperages

尺寸Φ/电流：

Current电流：AC/DC?(+) AC (OCV 70 amps)

Related Specification参考标准：H13 Tool Steel

Storage储存：Electrodes should be stored in dry conditions. Should the electrodes ?become damp, re-dry for one hour at 180°C before use. 焊条应储存在干燥环境中。如果焊条受潮，应在180°C下重新干燥1小时后再使用。