英国进口MWA特种钢焊条Mac Trode E66|E312-17|难焊钢|未知钢|异种钢焊接

Superior specially designed high strength austenitic type electrode of duplex structure. All purpose low amperage electrode. Easy to use with smooth arc, low spatter and even bead formulation. Can be used for overlaying and joining dissimilar steels to one another, high and low carbon steels, spring steels, chrome-nickel, vanadium steel, high speed steel, manganese steel, tool and die steels, cast steels, ferritic to austenitic steels and steels of unknown composition. It can also be used to form a primary buffer layer when building up a specially hard surface. High resistance to cracking coupled with good wear, heat, impact and corrosion resistance. Therefore this electrode has uses in practically every type of industry resulting in one of the most universally used electrodes for problem and unknown steels. Also available as a TIG and MIG wire.

Mac Trode E66为特殊设计高强度奥氏体型双相结构优质焊条。通用性广，电流低，使用方便，电弧平滑，飞溅少，焊缝成形均匀美观。可用于碳钢、弹簧钢、铬镍钢、钒钢、高速钢、锰钢、工模具钢、铸钢、铁素体-奥氏体双相钢等各种难焊钢以及成分未知钢等异种钢之间的堆焊和连接。当堆焊特别硬的表面时，它也可以用做缓冲层。抗裂性高，同时具有良好的耐磨、耐热、抗冲击和耐腐蚀性。该焊条几乎在所有类型行业中都有应用，焊接难焊钢和未知钢最为普遍使用的焊条之一。有对应TIG/MIG焊丝可供选择。

典型应用：工模具、泵轴、轮齿、壳体裂纹等修复，化工、建筑和采矿行业中使用的轴和叶片堆焊重建，以及断裂螺栓的拆除。硬质合金之前用作缓冲层。特别是可以用于未知母材金属的修复。

Typical All Weld Metal Chemical Analysis (%)

典型全焊缝金属成分

Typical All Weld Metal Mechanical Properties（As Welded）

典型全焊缝金属机械性能（焊态）：

Tensile Strength抗拉强度：840 N/mm²

Elongation延伸率： 25%

Hardness硬度： 220 HB

Sizes Available and Recommended Amperages

尺寸Φ/电流：

Current电流：AC/DC (+)

Related Specification参考标准：AWS A5.4 E312-17

Storage储存：Electrodes should be stored in dry conditions. Should the electrodes become damp, re-dry for one hour at 150°C before use. 焊条应储存在干燥环境中。如果焊条受潮，应在150°C下重新干燥1小时后再使用。

使用注意事项：

E66焊条保持干燥，防止气孔的产生。焊缝细化改善组织性能。

焊前待焊件表面清理干净。

如有必要，使用夹具、固定装置和定位焊缝使焊件固定。

厚型材焊接时开90°V形槽，对于坡口大的焊缝应采取多层焊接。

在焊接时焊接速度均匀。尽量短弧焊接，推荐使用线状焊道以防止过热。

焊渣冷却后再清除。

通常情况下不需要预热。如需预热，则根据工件的材料及尺寸来决定预热温度。比如焊接高碳钢时预热至150°C-200°C左右；焊接弹簧钢时冷焊接、以免弹簧软化。

使用过程中有任何问题，随时联系我们。